Tradename ò
Composition
Supplier

Properties

Function & Compounding

Grade 312
Zinc oxide
Perl Pigments, LLCï

ZnO-99.3%, Pb-.09%, Fe-.02%, CD-.03%, sulfur-.10%, insoluble-.08%.

Accelerator, activator, vulcanizer

Grade 318 American Process
Zinc oxide
Perl Pigments, LLCï

ZnO-99.3%, Pb-.09%, Fe-.02%, CD-.03%, sulfur-.10%, insoluble-.08%.

Accelerator, activator, vulcanizer

Grade 318T American Process
Zinc oxide treated
Perl Pigments, LLCï

ZnO-99.3%, Pb-.09%, Fe-.02%, CD-.03%, sulfur-.10%, insoluble-.08%.

Accelerator, activator, vulcanizer

Hallco CAOP
Calcium hydroxide/DOP dispersion
The HallStar Co.ï

Sp.gr. 1.05; (80% calcium hydroxide) finely dispersed in DOP; free flowing powder, dustless.

Recommended for mill and internal mixing; offers better dispersion and safety.

HT-10
Zinc oxide
Hydro Technologies (Canada)ï

General purpose ZnO; BET 8-11 m²; sp.gr. 5.6; cream to off-white powder

Medium surface area ZnO; NR and SR activator; semi-reinforcing and hiding pigment with higher activity; useful in adhesive formulations as a latex activator and supplemental gelling agent.

HT-2C
Zinc oxide
Hydro Technologies (Canada)ï

General purpose ZnO; BET 4-7 m²; sp.gr. 5.6; cream to off-white powder

NR and SR activator; semi-reinforcing and hiding pigment.

HT-3C
Zinc oxide
Hydro Technologies (Canada)ï

General purpose ZnO; BET 4-8 m²; sp.gr. 5.6; cream to off-white powder

NR and SR activator; semi-reinforcing and hiding pigment.

HT-Active
Zinc oxide
Hydro Technologies (Canada)ï

High surface area ZnO; BET 40 m²; sp.gr. 5.6; cream to off-white powder; zinc content > 97%; Pb content <25 ppm

A highly dispersible zinc oxide especially suited for semi-transparent and latex compounds; its higher activity benefits compounds with reduced zinc oxide content; when used at higher levels, improves compression set, crosslink density and reduces cure time.

HTR
Zinc oxide
Hydro Technologies (Canada)ï

High surface area ZnO; BET 30 m²; sp.gr. 5.6; cream to off-white powder; zinc content >97%; Pb content <25 ppm

Slightly lower in surface area than HT Active; highly dispersible zinc oxide especially suited for semi-transparent and latex compounds; its higher activity benefits compounds with reduced zinc oxide content; when used at higher levels, improves compression set, crosslink density and reduces cure time.

Innovox 95
Calcium oxide, surface treated
Birch Chemicals Limitedï

High purity calcium oxide, with consistent low particle size range and excellent dispersion, specifically packaged for rubber compounding.

An efficient desiccant/moisture absorber for all commonly used elastomers giving protection from porosity or blistering of rubber products which are produced in low or high-temperature cure systems. Available in pre-weighed sachets for direct mixer application.

Kenlastic K-13409
85% Am. ZnO/NBR
Flow Polymers LLCï

Sp.gr. 3.30

Activator - a dispersion of Am. ZnO in polymer form

Kenlastic K-13884
90% fumed litharge/PIB
Flow Polymers LLCï

Sp.gr. 4.91

Activator, a dispersion of fumed litharge in polymer form

Kenlastic K-16148
90% red lead/ECO
Flow Polymers LLCï

Sp.gr. 5.42

Activator, a dispersion of red lead in polymer form

Kenlastic K-21409
90% red lead/CPE
Flow Polymers LLCï

Sp.gr. 5.08

Activator, a dispersion of red lead in polymer form

Kenlastic K-25067
60% HSC litharge/EPM
Flow Polymers LLCï

Sp.gr. 4.82

Activator, a dispersion of HSC litharge in polymer form

Kenlastic K-6640
90% red lead/EPM
Flow Polymers LLCï

Sp.gr. 4.56

Activator, a dispersion of red lead in polymer form

Kenlastic K-6642
90% fumed litharge/EPM
Flow Polymers LLCï

Sp.gr. 4.71

Activator, a dispersion of fumed litharge in polymer form

Kenlastic K-8135
90% red lead/PIB
Flow Polymers LLCï

Sp.gr. 4.72

Activator, a dispersion of red lead in polymer form

Kenlastic K-8313
85% Am. ZnO/PIB
Flow Polymers LLCï

Sp.gr. 3.18

Activator - a dispersion of Am. ZnO in polymer form

Kenlastic K-8895
90% EP #41 white lead/EPM
Flow Polymers LLCï

Sp.gr. 3.93

Activator - a dispersion of EP #41 White Lead in polymer form